硼铁矿应用于高铬型钒钛矿烧结优化的实验研究

实验室条件下,研究了硼铁矿对高铬型钒钛矿烧结工艺及冶金性能的影响.研究表明:随着硼铁矿质量配比的升高,垂直烧结速度、成品率、转鼓指数、烧结杯利用系数、综合指标及低温还原粉化性能均呈先升高后降低的趋势,在硼铁矿质量配比为5.0%时,以上各指数均达到最高值,分别为28.84 mm·min-1,86.02%,61.2%,1.919 t·(m2·h)-1,363及90.76%,均优于未配加硼铁矿时的烧结矿性能.因此,烧结矿性能得以优化,可以为高炉冶炼提供更为优质的高铬型钒钛烧结矿.     

低品位钼精矿的钼提取研究

采用焙烧—氨浸—渣碱浸工艺对某低品位钼精矿进行钼提取的研究.结果表明,碳酸钠的加入能有效分解钼酸钙,提高钼的提取率.焙烧—氨浸阶段最优工艺条件为焙烧温度600℃,焙烧时间2 h,氨浸温度80℃,氨水过量系数1.4,碳酸钠用量467 kg/t,液固比4.浸出渣中的钼分别采用酸法(HCl)和碱法(Na2CO3+NaOH)进行提取.结果表明:酸法仅可回收渣中34.92%的钼,而且操作过程不易控制,不适合实际应用;碱法(Na2CO3+NaOH)处理工艺中碳酸钠用量533 kg/t,氢氧化钠用量433 kg/t.放大实验结果显示整个流程钼的回收率达到96.8%.     

Technique for advanced electrochemical oxidation treatment of nanofiltration concentrate of landfill leachate

Landfill leachate treated with combined process of ＂pretreatment ＋biological treatment ＋advanced treatment （NF）＂ to produce nanofiltration concentrate, which bio-chemical ratio （B/C） is less than 0.1 and CODer concentration is 2 000-2 500 mg/L, high salt content. Which cannot be discharged under existing environ- mental standards. According to analysis based on electrochemical advanced oxidation mechanism, a two-step electrochemical tech- nique was recommended. In the first step, a pulse electrochemical technique was adopted. With Fe as consumption electrode and current density of 10 mA/cm2, the pollutants were removed by means of Fenton reaction, electroflotation and electrocoagulation. In the second step, a double function electrode was used to per- form electrocatalytic oxidation by means of titanium metallic oxi- dates. In the condition that current density being 12.5 mA/cm2, the pollutants were further removed by oxidation and electrolytic deposition. Result shows that the removing rate of CODer, NH3-N and CI were 70%-85%, 90% and 25%, respectively; average value of B/C ratio increased from 0.09 to 0.38 and conductivity reduced by 10%.     

硫脲介质火焰原子吸收光谱法测定铅精矿中的金

介绍了用硫酸钠消除铅的干扰，在王水－硫脲介质中用火焰原子吸收光测定铅精矿中金新方法，试验结果表明：线性范围为０－５．０μｇ／ｍＬ，方法回收率为９５．６％－１０２．１％，相对标准偏差小于２．１％。     

带临界指数的蜕化p-Laplace方程解的存在性

在含有临界指数的p-Laplace方程，由于嵌入Hp^1.p（Ω）→L^p＊b（Ω，｜x｜^-α）不紧，如果直接运用标准变分方法去讨论其临界点的存在是比较困难的．为此，采用集中紧原理，证明了方程的非平凡解的存在性．     

以龙舌兰蔗渣作为还原剂使磁铁矿精矿有效地金属化

The reduction behavior and metallization degree of magnetite concentrate with agave bagasse were investigated in an inert atmosphere. The effects of temperature, biomass content, and residence time on reduction experiments and metallization degree were investigated by X-ray diffraction and scanning electron microscopy. Compared with other types of biomass, agave bagasse had lower contents of nitrogen, sulfur, and ash. X-ray diffraction analysis showed that the metallization degree improved with increasing temperature and biomass content. Complete metallization was achieved at 1100°C for 30 min with 65:35 and 50:50 ratios of the magnetite concentrate to the agave bagasse. These results demonstrate that agave bagasse promotes the efficient metallization of magnetite concentrate without the external addition of a reducing agent. Therefore, this biomass is a technical suitable alternative to replace fossil fuels in steelmaking.     

搅拌磨超细粉磨金精矿工艺的优化

研究了搅拌磨超细粉磨金精矿的工艺,考察了主要参数对粉磨效果的影响.结果表明,通过优化磨矿过程中各种影响因素,可以获得细度-20μm＞99%的金精矿产品.     

混合精矿体系中方铅矿与黄铁矿浮选分离的矿浆电化学（Ⅰ）─—方铅矿表面丁基黄原酸铅的电化学还原动力学

采用恒电流极化法首次研究了方铅矿表面丁基黄原酸铅的电化学还原动力学行为，测定了丁基黄原酸铅电化学还原的动力学参数（如过电位、传递系数及交换电流密度），建立了还原反应的动力学方程，证实在方铅矿表面丁基黄原酸铅的电化学还原反应是一个不可逆电化学过程，过电位高达３０８ｍＶ。     

pH值对浸矿细菌的活化以及金精矿脱砷的影响

通过在摇瓶中设定6个不同初始pH值梯度1.3,1.5,1.7,1.8,1.9,2.1,对细菌的活化以及高砷金精矿的脱砷浸出进行了研究.细菌活化阶段,HQ-0211菌在pH值1.3~1.9范围更加适应,活化速度快,氧化效果好.高砷金精矿细菌脱砷阶段,初始pH值在1.7~1.9范围最利于细菌浸矿,停滞期短,氧化速度快.初始pH值较高,为2.1时,细菌会较快进入衰亡期,不适于细菌浸矿.初始pH值较低,为1.3~1.5时,细菌适应停滞期长,氧化脱砷速度缓慢.     

基于气基直接还原-熔分的硼铁矿高效利用新工艺

实验室条件下,以含硼铁精矿为原料制备氧化球团,对含硼铁精矿气基竖炉直接还原-电炉熔分新工艺进行了研究.结果表明,含硼铁精矿是良好的造球原料,1 200℃下焙烧20 min后,成品球团抗压强度可达2 500 N以上,满足气基竖炉直接还原工艺要求.在H2与CO体积比大于2/5且温度在850~1 000℃条件下,含硼铁精矿氧化球团还原率达到95%的时间为15~60 min,还原膨胀率不高于15%.在高温下电热熔化DRI后硼和铁可以高效分离,硼、铁收得率均可达到98%以上,富硼渣中B2O3的质量分数在21%以上,活性可达89%左右,是"一步法"生产硼酸的优良原料.含硼铁精矿气基竖炉直接还原电炉熔分新工艺可以实现硼铁高效分离和清洁利用.